Two Sides Heat Transparent PLA Shrink Film

Product Intrduction

PLA film is 100% biodegradable film, which is completely biodegradable and meets the certification of EN1343 and industrial composting. It offers exceptional clarity and stiffness similar to traditional OPP. It's a clear option for brands looking to improve the sustainability of their packaging.

Product Technical Data Sheet

这里可以自定义设置

Properties		Unit	Data		Test Method
Thickness (Tolerance : ±10%)		μm	25~40		ASTM D374
Tensile Strength		MPa	MD	TD	ASTM D882
			75	84
Elongation		%	MD	TD	ASTM D882
			110	117
Heat Shrinkage (100℃/10min)		%	MD	TD	---
			6	2.5
Heat Sealing Strength		N/15mm	4.61		85℃/80℃/135Kpa/25
Transmittance		%	93.5		ASTM D1003
Density		g/㎤	1.25		ASTM D792
Haze		%	0.7		ASTM D1003
Gloss		%	80		ASTM D2457
Dyne		mN/m	≥36		ASTM D2578
Coefficient of Friction	μs	-	0.55		ASTM D1894E
	μk		0.57

Product Structure

PLA-1031: is one side heat sealable transparent PLA film, which is designed to designed to cover a wide range of food and non-food packaging applications, using existing converting and packaging technologies. It is in the structure of three layers as follows:

Product Advantage

1. Transparency Comparison

2. Production Process Comparison

3. Raw Material Comparison

Product Characters

Good flatness & excellent glossy, Can be used for printing, metallizing, laminating and other packaging materials;

Safe, healthy, environment- friendly .Can be degraded into H2O and CO2 by micro organisms in landfill or water, remaining zero harmful substance in soil and water, totally non-toxic

Food grade biodegradable film for food packaging.also can be used for food grade coated paper

Good printability, easily adapt to various printing method;

Good heat sealing performance, especially suitable for high flash wave,ultrasonic hot sealing wave.

Product Application

Transparent PLA film used for packing fresh Flowers or books ,can be heat sealing for making bags, can be used for cup film, self-sealing bag ,flat pocket, etc. It has good air breathability and can be used in the anti-fog packaging of vegetable.

PLA’s Composting Process

1. Evolution of the temperature

The figure of the temperature shows the temperature evolution during the disintegration test. The temperature remained well above 40°C during 8 consecutive weeks.

2. Evolution of the Oxygen concentration

It shows the oxygen concentration in the exhaust air. The oxygen concentration remained always above 10%, except once after 8 days with a value of 7.4%. However, immediate action was undertaken and the oxygen concentration increased.

3. Visual presentation of the evolution of the disintegration of PLA Shrink film

PLA-1031 Two Sides Heat Sealable Transparent PLA Film